Polymer concrete protective coating.¡ª¡ªHC

   This product is the combination of organic matter and inorganic matter mixed resin and resin for the synthesis of stage functional filler.Slurry protective layer,With alkali resistance MMA The resin is mixed with polyurethane resin and silicone resin.Forming the core structure of latex resin.This structure is superior to other coatings in terms of physical properties and weather resistance.Use of this product£¨metal alkoxide£©the coating is formed by hydrolysis and condensation polymerization.¡£

 Usage

  The concrete is exposed to natural conditions for a long time.Exposed to sunlight, rain, snow, snow melt, etc.As time goes by, the concrete surface appears to be sand, falling off, showing gluten, damage and other diseases.There is a lot of trouble in curing concrete,Due to the defects of the original paint, the quality problems such as peeling and peeling will occur after a period of time.Durability is not guaranteed, and the presence of the polymer concrete protective coating, HC, will solve this problem.

1) Transportation related facilities.The outer walls of Bridges, viaducts, tunnels, concrete pavements, underground roads, bus stations, airports, and harbors - Marine facilities.

2) Building civil facilities.Public housing, various buildings, education facilities, sports facilities, public areas and external walls of various facilities.

3)Factories and storage facilities.Food factories, pharmaceutical factories and other factories, complete sets of facilities, grain warehouses and cold storage, various concrete building external walls.

Performance

1£©Model: 1 liquid grey latex.

2£©Cure time: 3 hours (20 ¡æ)

3£©For subsequent engineering before need time: 3 hours (20 ¡æ)

4£©Consumption: 200g/m2(T=250um)5£©°ü×°µ¥Î»£º20kg

6£©Specific gravity: 1.180

7£©Solids: 65%.

Characteristics

1. Alkaline recovery and interfacial adhesion intensifier (covering TRET)

Liquid ceramic modified silicate as the main material of the product.With excellent capillary permeability, the internal natural catalyst solidifies into ceramic structure.The concrete structure is strengthened to enhance the strength of the concrete surface.

2.Reinforcement antirust mortar (CBA)

Special cement and hard silica sand, antirust additive composition of the mortar products, close to the surface of the steel, forming a tight protective film, blocking the humidity. It has the characteristics of strengthening the adhesion of repairing

3.Repair reinforced mortar (slurry pulp) 

It belongs to the cement mortar, the flow flat powder resin and the hard aggregate to add the surface modification of the PE fiber to the levelness, strengthen the stretching strength, prevent the crack. Because of its excellent water tightness, improve the surface water resistance, is a carbon - resistant, chemical - resistant

4. Repair of protective mortar (covering 100)

Made of fine cement, ceramic particles and other inorganic sand products, it belongs to the coating of equipment coating, the structure is meticulous, the durability is excellent, long-term maintenance concrete surface.

4. Mixed coating material (HC)

  The core structure of latex resin is formed by the combination of polyurethane resin and silicone resin. This structure is superior to other coatings in terms of physical properties and weather resistance.

The construction method

1£©Concrete bottom adjustment.

Clean aging concrete surfaces with scraping plates; (grinding work and removing grease spots, stains, etc.)

2£©Construction of the primer

Apply primer before applying neutral protective coating;

3£©Construction of slurry protection layer.

When spraying, the spraying machine is kept at a distance of 25cm, and the spray gun is vertical and evenly sprayed.

4£©Maintenance

After fully curing the coating to carry on the follow-up project;